Printing, lamination & pouching application.
Transparent, both side heat sealable, one side corona treated CPP film with an excellent barrier, clarity, slip and antistatic properties for single or two ply printing laminate application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesive during conversion.
| PROPERTIES | TEST METHOD | UNIT | AC18H1 | AC20H1 | AC25H1 | AC30H1 | AC35H1 | AC40H1 |
|---|---|---|---|---|---|---|---|---|
| Physical | ||||||||
| Thickness | ASTM D 374 | Micron | 18 | 20 | 25 | 30 | 35 | 40 |
| Grammage | ATM | gm/m2 | 16.38 | 18.2 | 22.75 | 27.3 | 31.85 | 36.4 |
| Yield | ATM | m2/kg | 61.0 | 55.0 | 44.0 | 36.6 | 31.4 | 27.4 |
| Surface | ||||||||
| Treatment Level (Min) Metallisable Side |
ASTM D 2578 | dyne/cm | 38 | 38 | 38 | 38 | 38 | 38 |
| Optical | ||||||||
| Haze (Max) | ASTM D 1003 | % | 3.5 | 4.0 | 4.0 | 4.5 | 4.5 | 5.0 |
| Gloss (Min) at 450 Angle |
ASTM D 2457 | - | 80 | 80 | 80 | 75 | 70 | 70 |
| Mechanical | ||||||||
| Coefficient of Friction (Max) |
ASTM D 1894 | Static Kinetic |
0.30 0.25 |
0.30 0.25 |
0.30 0.25 |
0.30 0.25 |
0.30 0.25 |
0.30 0.25 |
| Tensile Strength(Min) |
ASTM D 882 | kg/cm2MD TD |
500 220 |
500 220 |
500 220 |
500 210 |
500 210 |
500 200 |
| Modulus (Min) | ASTM D 882 | kg/cm2MD TD |
- | - | - | - | - | - |
| Elongation (Max) | ASTM D 882 | % MD TD |
450 600 |
450 600 |
450 600 |
450 600 |
450 600 |
450 600 |
| Thermal | ||||||||
| Shrinkage (Max) at 1200C/5 min |
ATM | % MD TD |
3.0 2.0 |
3.0 2.0 |
3.0 2.0 |
3.0 2.0 |
3.0 2.0 |
3.0 2.0 |
| Seal Initiation Temperature (Max) 2 Bar / 1 Sec |
ATM | 0C | 115-125 | 115-125 | 115-125 | 115-125 | 115-125 | 115-125 |
| Sealing Strength (Min) at 1200C /2 Bar/ 1 Sec |
ATM | gms/25mm | 600 | 600 | 600 | 600 | 600 | 600 |
| Barrier | ||||||||
| Water Vapour Transmission Rate |
ASTM E 398 | gm/m2/24h | 14 | 13 | 12 | 11 | 11 | 10 |
| Oxygen Gas Transmission Rate |
ASTM E 3985 | cc/m2/24h | 3800 | 3800 | 3750 | 3700 | 3650 | 3650 |
| The values given in this technical datasheet are typical performance data and are believed to be accurate. These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. AAKASH POLY FILMS LIMITED suggests the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any particular use. | ||||||||
Storage & Handling: Temperature should preferably be less than 30⁰C & Humidity 55±5% in the storage area and material should be consumed with three months of receipt.
ATM: Aakash Test Method, MD: Machine Direction, TD: Transverse Direction